Fabrication of all-solid-state rechargeable lithium-ion battery using mille-feuille structure of Li0.35La0.55TiO3

作者：Kotobuki Masashi^*; Munakata Hirokazu; Kanamura Kiyoshi

来源：Journal of Power Sources, 2011, 196(16): 6947-6950.

DOI：10.1016/j.jpowsour.2010.11.139

• All-solid-state Li ion battery
• 3D battery
• 3DOM structure
• Solid electrolyte

A mille-feuille structure, which comprises both sides of dense layer are sandwiched by porous layers, is one of the promising structures for 3-dimensional (3D) all-solid-state battery. The porous layers should have 3-dimensionally ordered macroporous structure to obtain large contact area between electrolyte and electrode. Li0.35La0.55TiO3 (LLT) solid electrolyte with the mille-feuille structure was fabricated by the suspension filtration method. The dense layer was sintered well, no grain boundary was observed. The porous layers contacted well with dense layer. Thicknesses of dense and porous layers were 30 and 26 mu m, respectively. To check compatibility of the mille-feuille LLT with all-solid-state Li ion battery, chronopotentiometry of symmetric cell with LiMn2O4/mille-feuille LLT/LiMn2O4 configuration was measured. Charge and discharge currents were clearly observed, indicating that the cell was successfully operated.

• 出版日期2011-8-15