Processing of Intermetallic Titanium Aluminide Wires

作者：Marr Tom; Freudenberger Jens^*; Kauffmann Alexander; Romberg Jan; Okulov Ilya; Petters Romy; Scharnweber Juliane; Eschke Andy; Oertel Carl Georg; Kuehn Uta; Eckert Juergen; Skrotzki Werner; Schultz Ludwig

来源：Metals, 2013, 3(2): 188-201.

DOI：10.3390/met3020188

• Ti
• Al
• titanium aluminide
• wire
• phase reaction

This study shows the possibility of processing titanium aluminide wires by cold deformation and annealing. An accumulative swaging and bundling technique is used to co-deform Ti and Al. Subsequently, a two step heat treatment is applied to form the desired intermetallics, which strongly depends on the ratio of Ti and Al in the final composite and therefore on the geometry of the starting composite. In a first step, the whole amount of Al is transformed to TiAl3 by Al diffusion into Ti. This involves the formation of 12% porosity. In a second step, the complete microstructure is transformed into the equilibrium state of gamma-TiAl and TiAl3. Using this approach, it is possible to obtain various kinds of gradient materials, since there is an intrinsic concentration gradient installed due to the swaging and bundling technique, but the processing of pure gamma-TiAl wires is possible as well.

• 出版日期2013-6