Preparation and properties of adjacency crosslinked polyurethane-urea elastomers

作者：Wu, Yuan; Cao, Yu-Yang; Wu, Shou-Peng; Li, Zai-Feng^*

来源：Frontiers of Materials Science, 2012, 6(4): 347-357.

DOI：10.1007/s11706-012-0184-2

• HTBN
• PUU
• crosslinking
• HVA-2
• thermal property
• FT-IR

Adjacency crosslinked polyurethane-urea (PUU) elastomers with different crosslinking density were prepared by using hydroxyl-terminated liquid butadiene-nitrile (HTBN), toluene diisocyanate (TDI) and chain extender 3,5-dimethyl thio-toluene diamine (DMTDA) as raw materials, dicumyl peroxide (DCP) as initiator, and N, N'-m-phenylene dimaleimide (HVA-2) as the crosslinking agent. The influences of the crosslinking density and temperature on the structure and properties of such elastomers were investigated. The crosslinking density of PUU elastomer was tested by the NMR method. It is found that when the content of HVA-2 is 1.5%, the mechanical properties of polyurethane elastomer achieve optimal performance. By testing thermal performance of PUU, compared with linear PUU, the thermal stability of the elastomers has a marked improvement. With the addition of HVA-2, the loss factor tand decreases. FT-IR spectral studies of PUU elastomer at various temperatures were performed. From this study, heat-resistance polyurethane could be prepared, and the properties of PUU at high temperature could be improved obviously.

• 出版日期2012-12
• 单位青岛科技大学