Microstructure and electric properties of Nb doping x(Ba0.7Ca0.3)TiO3-(1-x)Ba (Zr0.2Ti0.8)O3 ceramics

作者：Zhang, C. H.; Chi, Q. G.; He, X. X.; Lin, J. Q.^*; Chen, Y.; Liu, L. Z.; Lei, Q. Q.

来源：Journal of Alloys and Compounds, 2016, 685: 936-940.

DOI：10.1016/j.jallcom.2016.06.203

• Powders: solid state reaction
• Grain size
• Structure
• Electrical properties
• BaTiO3 and titanates

In this paper, t mol% Nb2O5 doped x(Ba0.7Ca0.3)TiO3-(1-x)Ba(Zr0.2Ti0.8)O-3 [xBCT-(1-x)BZT-t mol% Nb2O5] lead-free piezoelectric ceramics were prepared successfully using a solid-state reaction technique. Firstly, the phase transition of xBCT-(1-x) BZT ceramics were investigated, and it was found that 0.47BCT-0.53BZT sample shows a rhombohedral (R)-tetragonal (T) phase transition at room temperature near Morphotropic Phase Boundary and presents better ferroelectric and piezoelectric properties compared with the other component ceramics. On this basis, the crystal structure, surface morphologies and electrical properties of the Nb2O5 doped 0.47BCT-0.53BZT ceramic were studied in detail. It was found the grain size increases monotonously and the microstructure become more denser and homogeneous when Nb-doping concentration increases above t = 0.3, and a maximum strain value of 0.132% was obtained at E = 20 kV/cm. Additionally, the excellent electric properties with a high remanent polarization (P-r = 8.3 mu C/cm(2)), a low coercive field (E-c = 1.55 kV/cm) were also obtained on 0.47BCT -0.53BZT-0.3 mol% Nb2O5 lead-free ceramics, which is promising for application in lead-free practical applications.

• 出版日期2016-11-15
• 单位哈尔滨学院