An atmospheric pressure helium and oxygen plasma has been used for the surface preparation of 410 stainless steel and carbon-fiber epoxy laminates prior to bonding to themselves or to each other. Lap shear results for stainless steel coupons and carbon-fiber epoxy laminates demonstrated an 80% and a 150% increase in bond strength, respectively, after plasma activation. Following 7 days of aging, wedge crack extension tests revealed a crack extension length of 7.0mm and 2.5mm for the untreated and plasma-activated steel. The untreated stainless steel had 30% cohesive failure compared to 97% for steel activated with the plasma. Surface analysis by X-ray photoelectron spectroscopy showed that carbonaceous contamination was removed by plasma treatment, and specific functional groups, e.g. carboxylic acids, were formed on the surface. These functional groups promoted strong chemical bonding to the epoxy film adhesive. Atmospheric pressure plasmas are an attractive alternative to abrasion techniques for surface preparation prior to bonding.
- 出版日期2014-1