Mechanical and thermal properties of LaMgAl11O19

作者：Jiang B; Fang M H^*; Huang Z H; Liu Y G; Peng P; Zhang J

来源：Materials Research Bulletin, 2010, 45(10): 1506-1508.

DOI：10.1016/j.materresbull.2010.06.014

• Inorganic compounds
• Microstructure
• Mechanical properties
• Thermal conductivity

Lanthanum magnesium hexaaluminate (LaMgAl11O19) powders were synthesized successfully at 1300 degrees C for 4 h by solid-state reaction, and LaMgAl11O19 ceramic was prepared at 1700 degrees C for 6 h by pressureless sintering. Phase composition, microstructure, mechanical and thermophysical properties of LaMgAl11O19 ceramic were investigated. Results show that the flexural strength and fracture toughness of LaMgAl11O19 ceramic are 353.3 +/- 12.5 MPa and 4.60 +/- 0.46 MPa m(1/2). Young's Modulus and Poisson ratio is 295 GPa and 0.23, respectively. The linear thermal expansion coefficient of LaMgAl11O19 ceramic from 473 K to 1473 K is 9.17 x 10(-6)/K, and thermal conductivity at 1273 K is 2.55 W/m K.