High-field magnetization of a DyFe5Al7 single crystal

作者：Gorbunov D I^*; Andreev A V; Skourski Y; Kuz' min M D

来源：Journal of Alloys and Compounds, 2013, 553: 358-363.

DOI：10.1016/j.jallcom.2012.11.083

• Rare-earth intermetallics
• Magnetic anisotropy
• Ferrimagnetism
• High magnetic fields
• Field-induced transition

The magnetization of a DyFe5Al7 single crystal with the tetragonal ThMn12-type structure was measured in pulsed fields up to 60 T along the principal axes. The compound orders ferrimagnetically at T-C = 231 K and exhibits a compensation of the Dy and Fe sublattices at T-comp = 93 K. DyFe5Al7 displays a high magnetic anisotropy of the easy-plane type, the [100] axis is the easy magnetization direction with the spontaneous magnetic moment M-s = 2.1 mu(B)/f.u. at T = 2 K. In a field applied along the easy axis, two field-induced hysteretic transitions are observed at 30 and 53 T at T = 2 K. The critical field H-cr1 of the first transition depends strongly on temperature, whereas H-cr2 is practically temperature-independent. Above the transitions the magnetization continues to grow as a function of field, as the sublattice moments continue to rotate. To reach the full saturation (forced ferromagnetic state), fields of several Tesla higher than 60 T are required. The field dependence of magnetization along the easy [100] axis was analyzed within a model for a ferrimagnet with an anisotropic dominant sublattice. The model correctly reproduces the behavior of magnetization in a magnetic field. The intersublattice molecular field on Dy and the basal-plane anisotropy constant of the Dy sublattice have been determined.

• 出版日期2013-3-15