Adsorption characteristics of propan-2-ol vapours on activated carbon Sorbonorit 4 in electrothermal temperature swing adsorption process

作者：Downarowicz D^*

来源：Adsorption, 2015, 21(1-2): 87-98.

DOI：10.1007/s10450-015-9652-1

• Adsorption
• Activated carbon
• Electrothermal regeneration
• IPA
• Thomas model
• XPS

Adsorption characteristics of propan-2-ol on Sorbonorit 4 activated carbon were determined using the breakthrough curve tests in a cyclic electrothermal temperature swing adsorption process. Maximum adsorption capacity, breakthrough time, throughput ratio and length of unused bed were also evaluated. As a result of multiple regeneration, the adsorption capacity of Sorbonorit 4 increased. Electrothermally-induced changes in the internal structure of Sorbonorit 4 and in the chemical composition of its surface were assessed based on adsorption equilibrium measurements by the gravimetric method and X-ray photoelectron spectroscopy (XPS). Three samples of virgin, direct resistively heated and electrothermally regenerated Sorbonorit 4 were used. The structural characteristics of activated carbon show that that fresh and direct resistive heated Sorbonorit 4 has a bimodal structure. Regenerated activated carbon contains one fraction of micropores. XPS analysis revealed that the same hydroxyl, carbonyl and carboxyl groups were found on the surface of all Sorbonorit 4 samples, albeit in different volume ratios. Regenerated Sorbonorit 4 has higher adsorption capacity than pure adsorbent while resistively heated Sorbonorit 4 displays lower adsorption efficiency.

• 出版日期2015-2