Decoupling of the softening processes during rapid tempering of a martensitic steel

作者：Biro Elliot; McDermid Joseph R^*; Vignier Samuel; Zhou Y Norman

来源：Materials Science and Engineering A-Structural Materials Properties Microstructure and Processing, 2014, 615: 395-404.

DOI：10.1016/j.msea.2014.07.102

• Martensite
• Tempering
• Transformation kinetics
• HAZ softening

The increased adoption of martensite-containing advanced high strength steels, such as martensitic and dual-phase steels, into automotive applications has led to concerns among practitioners with respect to softening during rapid tempering cycles such as those experienced during laser welding. Past studies on rapid tempering have successfully modeled the rapid tempering process; however, the activation energies and softening rates calculated did not match the classic literature values associated with martensite tempering. The present study examined rapid tempering data for a martensitic steel and separated the softening process into two stages: carbide nucleation and carbide coarsening or growth. The activation energies calculated for each process were found to be consistent with classic literature values for diffusion controlled nucleation and growth of carbides during martensite tempering.

• 出版日期2014-10-6