Austenite Transformation Behaviour of 2205 Duplex Stainless Steels under Hot Tensile Test

作者:Li Hongfei*; Fan Guangwei; He Yan; Bai Jingang; Zhang Caili; Han Peide
来源:Steel Research International, 2015, 86(1): 84-88.
DOI:10.1002/srin.201400032

摘要

The aim of the present work was to evaluate initial secondary austenite phase microstructural changes (delta > gamma') in 2205 duplex stainless steel with N content of 0.36 wt% during hot tensile test. The results showed there is no secondary austenite microstructural change in zero deformation degree. The secondary austenite (gamma(2)) phase transformation occurred only in the cooling process and under hot deformation condition. Initial secondary austenite (gamma') occurred within the ferrite matrix at the temperature range of 950-1150 degrees C. The precipitation of initial gamma' increased with the increase in aging time and deformation degree. With increasing time, a progressive transformation of initial gamma' to gamma(2) occurred. The orientation relationship between the initial gamma' phase and the d matrix was different at varying high temperatures. A significant change in the hot deformation condition has been observed as a consequence of secondary austenite reformation. These results indicated the importance of control over the shape and volume fraction of secondary austenite phases on high nitrogen duplex stainless steels to improve hot ductility.