A simple and efficient method for the synthesis of SiBNC ceramics with different Si/B atomic ratios

作者：Ji, Xiaoyu; Shao, Changwei^*; Wang, Hao^*; Wang, Jun; Cheng, Jun; Long, Xin; Mao, Tengfei

来源：Ceramics International, 2017, 43(10): 7469-7476.

DOI：10.1016/j.ceramint.2017.03.022

• SiBNC ceramics
• Polymer
• Si/B ratio
• Crystallization
• High temperature

The high-temperature durability of SiBNC ceramics is significantly influenced by Si/B ratios and the synthetic procedures. Single-source synthetic routes can yield homogeneous ceramics at the atomic level, but the Si/B ratio cannot be efficiently adjusted. In this paper, a simple and efficient method for the synthesis of SiBNC precursor polyborosilazanes (PBSZs) with different Si/B ratios has been established via a one-pot reaction involving boron trichloride, dichloromethylsilane and hexamethyldisilazane in different molar ratios. The Si/B ratios of the derived SiBNC ceramics were consistent with that of the precursor PBSZs. When pyrolysed at 1000 degrees C, PBSZs with 0.52, 0.94 and 2.12 Si/B ratios transformed into SiB2.6N5C2.2, SiB0.9N2.7C1.3 and Si2BN3C1.4 ceramics respectively. The polymer-to-ceramic process was also studied and featured ceramic yields of 43.2 wt%, 50.1 wt% and 62.2 wt%, respectively. The derived ceramic SiB0.9N2.7C1.3 resisted crystallization up until 1700 degrees C, whereas the SiB2.6N5C2.2 and SiB2BN3C1.4 could remain amorphous up to 1600 degrees C only. Using the precursor with 0.94 Si/B ratio, the SiBNC ceramic fibres were also obtained.

• 出版日期2017-7
• 单位中国人民解放军国防科学技术大学