A study of pressureless microwave sintering, microwave-assisted hot press sintering and conventional hot pressing on properties of aluminium/alumina nanocomposite

作者：Abedinzadeh Reza^*; Safavi Seyed Mohsen; Karimzadeh Fathallah

来源：Journal of Mechanical Science and Technology, 2016, 30(5): 1967-1972.

DOI：10.1007/s12206-016-0402-4

• Microwave-assisted hot press sintering
• Nanomaterial
• Metallic matrix composite
• Nanoindentation
• Hardness
• Elastic modulus

Bulk Al/4wt-%Al2O3 nanocomposites were prepared by consolidating nanocomposite powders using pressureless microwave sintering, microwave-assisted hot press sintering and conventional hot pressing techniques. Microstructural observations revealed that the microwave- assisted hot press sintering at different sintering temperatures of 400A degrees C and 500A degrees C resulted in more densification and smaller grain size for Al/Al2O3 nanocomposite as compared with the conventional hot pressing. Moreover, the application of pressure in microwave sintering process led to more densification and grain growth. Mechanical properties resulting from microhardness and nanoindentation tests were also compared between three-method processed samples. It was found that the microwave-assisted hot-pressed sample exhibited higher hardness and elastic modulus in comparison with microwave-sintered and conventional hot-pressed samples. The improvement in the mechanical properties can be ascribed to lower porosity of microwave-assisted hot-pressed sample.

• 出版日期2016-5