A comprehensive study on the kinetics of aqueous free-radical homo- and copolymerization of acrylamide and diallyldimethylammonium chloride by online H-1-NMR spectroscopy

作者：Abdollahi Mahdi^*; Alamdari Parisa; Koolivand Hadis; Ziaee Farshid

来源：Journal of Polymer Research, 2013, 20(10): 239.

DOI：10.1007/s10965-013-0239-9

• Acrylamide
• Diallyldimethylammonium chloride
• Free-radical copolymerization
• Polymerization kinetics
• Reactivity ratio
• Composition drift

Free-radical homo-and copolymerization of acrylamide (AAm) and diallyldimethylammonium chloride (DADMAC) initiated with potassium persulfate (KPS) were performed in the presence of 0.1 M NaCl solution in D2O at 50 degrees C. Online H-1-NMR kinetic experiments were used to study polymerization kinetics via determination of the individual and overall conversion of the comonomers and compositions of the comonomer mixture and produced copolymer as a function of the reaction time. Reactivity ratios of the AAm and DADMAC were calculated by Mao-Huglin (MH) and extended Kelen-Tudos (KT) methods to be 7.0855 +/- 1.3963, 0.1216 +/- 0.0301 and 6.9458 +/- 2.0113, 0.1201 +/- 0.0437 respectively. %26quot;Lumped%26quot; kinetic parameter (k(p)k(t)(-0.5)) was estimated from experimental data. Results showed that k(p)k(t)(-0.5) value increases by increasing mole fraction of the AAm in the initial reaction mixture. Drift in the comonomer mixture and copolymer compositions with reaction progress was evaluated experimentally and theoretically. Theoretical values were calculated from Meyer-Lowry equation by using reactivity ratios obtained from MH method. A good fitting between the experimental and theoretical values was observed, indicating accuracy of the reactivity ratios estimated in the present work. It was found from following changes in the copolymer composition with the comonomer conversion that produced copolymer has a statistical structure.

• 出版日期2013-9-5