摘要
In this paper, Mn3Ga2 alloys with high saturation magnetization and high Curie temperatures were prepared by levitation melting high pure Mn and Ga elements followed by annealing. The effect of annealing temperature on phase structure and magnetic properties was investigated by means of x-ray diffraction and a vibrating sample magnetometer. A single phase alloy Mn3Ga2, which has tetragonal P4/mmm structure, was obtained with an annealing temperature of 773K and annealing time of 24 h. The hysteresis curve of its easy axis for this single phase alloy shows that the room temperature coercivity and saturation magnetization are 4.18 kOe and 50.81 emu/g, respectively. The thermomagnetic curves indicate that the Curie temperature is about 650K and a phase transformation occurs above 823K.
- 出版日期2014-5-7
- 单位北京工业大学