Ultrafast Flame Annealing of TiO2 Paste for Fabricating Dye-Sensitized and Perovskite Solar Cells with Enhanced Efficiency

作者：Kim Jung Kyu; Chai Sung Uk; Cho Yoonjun; Cai Lili; Kim Sung June; Park Sangwook; Park Jong Hyeok^*; Zheng Xiaolin^*

来源：Small, 2017, 13(42): UNSP 1702260.

DOI：10.1002/smll.201702260

• dye-sensitized solar cells
• fast metal oxide sintering
• flame annealing
• perovskite solar cells
• TiO2 photoelectrodes

Mesoporous TiO2 nanoparticle (NP) films are broadly used as electrodes in photoelectrochemical cells, dye-sensitized solar cells (DSSCs), and perovskite solar cells (PSCs). State-of-the-art mesoporous TiO2 NP films for these solar cells are fabricated by annealing TiO2 paste-coated fluorine-doped tin oxide glass in a box furnace at 500 degrees C for approximate to 30 min. Here, the use of a nontraditional reactor, i.e., flame, is reported for the high throughput and ultrafast annealing of TiO2 paste (approximate to 1 min). This flame-annealing method, compared to conventional furnace annealing, exhibits three distinct benefits. First, flame removes polymeric binders in the initial TiO2 paste more completely because of its high temperature (approximate to 1000 degrees C). Second, flame induces strong interconnections between TiO2 nanoparticles without affecting the underlying transparent conducting oxide substrate. Third, the flame-induced carbothermic reduction on the TiO2 surface facilitates charge injection from the dye/perovskite to TiO2. Consequently, when the flame-annealed mesoporous TiO2 film is used to fabricate DSSCs and PSCs, both exhibit enhanced charge transport and higher power conversion efficiencies than those fabricated using furnace-annealed TiO2 films. Finally, when the ultrafast flame-annealing method is combined with a fast dye-coating method to fabricate DSSC devices, its total fabrication time is reduced from over 3 h to approximate to 10 min.

• 出版日期2017-11-13