AC over-current characteristics of YBCO coated conductor with copper stabilizer layer considering insulation layer

作者：Du H I^*; Kim M J; Kim Y J; Lee D H; Han B S; Song S S

来源：Physica C-Superconductivity and Its Applications, 2010, 470(20): 1626-1630.

DOI：10.1016/j.physc.2010.05.176

• YBCO coated conductor
• Stabilizer layer
• BSCCO wire
• HTS cable
• Over-current
• Transport current property

Compared with the first-generation BSCCO wire, the YBCO thin-film wire boasts low material costs and high J(c) and superior magnetic-field properties, among other strengths. Meanwhile, the previous BSCCO wire material for superconducting cables has been researched on considerably with regard to its post-wire quenching characteristics during the application of an alternating over-current. In this regard, the promising YBCO thin-film wire has yet to be further researched on. Moreover, still lacking is research on the YBCO thin-film wire with insulating layers, which is essential in the manufacture of superconducting cables, along with the testing of the application of an alternating over-current to the wire.
In this study, YBCO thin-film wires with copper-stabilizing layers were used in testing alternating over-current application according to the presence or absence of insulating layers and to the thickness of such layers, to examine the post-quenching wire resistance increase and quenching trends. The YBCO thin-film wire with copper-stabilizing layers has a critical temperature of 90 K and a critical current of 85 A(rms). Moreover, its current application cycle is 5.5 cycles, and its applied currents are 354, 517, 712, and 915 A(peak). These figures enabled the YBCO thin-film wires with copper-stabilizing layers to reach 90, 180, 250, and 300 K. respectively, in this study. These temperatures serve as a relative reference to examine the post-quenching wire properties following the application of an alternating over-current.