High pressure behavior of nano-crystalline CeO2 up to 35 GPa: a Raman investigation

作者：Dogra Sugandha; Sharma Nita Dilawar^*; Singh Jasveer; Poswal Himanshu Kumar; Sharma S M; Bandyopadhyay A K

来源：High Pressure Research, 2011, 31(2): 292-303.

DOI：10.1080/08957959.2011.576674

• high pressure
• phase transitions
• Raman spectroscopy
• CeO2

The present paper reports the results of in situ Raman studies carried out on nano-crystalline CeO2 up to a pressure of 35GPa at room temperature. The material was characterized at ambient conditions using X-ray diffraction and Raman spectroscopy and was found to have a cubic structure. We observed the Raman peak at ambient at 465cm-1, which is characteristic of the cubic structure of the material. The sample was pressurized using a diamond anvil cell using ruby fluorescence as the pressure monitor, and the phase evolution was tracked by Raman spectroscopy. With an increase in the applied pressure, the cubic band was seen to steadily shift to higher wavenumbers. However, we observed the appearance of a number of new peaks around a pressure of about 34.7GPa. CeO2 was found to undergo a phase transition to an orthorhombic -PbCl2-type structure at this pressure. With the release of the applied pressure, the observed peaks steadily shift to lower wavenumbers. On decompression, the high pressure phase existed down to a total release of pressure.

• 出版日期2011