Adsorption energy distribution of carbon tetrachloride on carbon nanofiber arrays prepared by template synthesis

作者：Wu Chi Hsin; Shr Jin Fang; Wu Chu Fu; Hsieh Chien Te^*

来源：Physica E: Low-Dimensional Systems and Nanostructures , 2008, 40(4): 814-821.

DOI：10.1016/j.physe.2007.10.020

• carbon nanofiber
• template synthesis
• adsorption
• adsorption energy distribution
• pore size distribution

The influence of pore size distribution on adsorption energy distributions (AEDs) of aligned carbon nanofiber (CNF) arrays in vapor phase was conducted in the present study. A template-assisted synthesis was employed to fabricate aligned CNF arrays with different pore size distributions (PSDs). Adsorption isotherms Of CCl4 onto the CNF arrays were investigated within an entire pressure of 0.05-0.18 atm at 30 degrees C. The adsorptive surface coverage was found to decrease with the average pore size, indicating the presence of heterogeneity for gas adsorption. An AED model was postulated to describe the heterogeneous surface consisting of numerous surface pitchwises that obey a localized Langmuir model. It was found that all CNF arrays exhibit a similar Gaussian-type AED, in where the peak adsorption energy shifts to a higher energy with decreasing the pore size of CNFs. This finding can be ascribed to a fact that micropores are major providers of adsorption sites, whereas in mesopores only weaker adsorption is observed, thus resulting in the shift of energy distribution. An excellent prediction to the adsorption isotherms Of CCl4 by the AED model indicates that the PSD of CNFs acts a crucial factor in affecting the adsorptive coverage.

• 出版日期2008-2