Microstructure, thermal physical property and surface morphology of W-Cu composite fabricated via selective laser melting

作者：Yan, Anru^*; Wang, Zhiyong; Yang, Tiantian; Wang, Yanling; Ma, Zhihong

来源：Materials and Design, 2016, 109: 79-87.

DOI：10.1016/j.matdes.2016.07.049

• W-Cu composite
• Selective laser melting
• Densification mechanism
• Microstructures
• Thermal properties
• Surface morphology

In this work, the W-(Ni)-Cu composites were fabricated by Selective Laser Melting with the different W content up to 80 wt.%. The effects of relative density, microstructure on thermal conductivity, thermal expansion coefficient, roughness and hardness of W-(Ni)-Cu composites were evaluated. The results indicate that during SLM W-(Ni)-Cu composites, there are two kinds of densification mechanism reflected on the microstructure characteristic. Rearrangement densification favors to achieve higher relative density, dense compact Cu matrix and a homogeneous distribution of W solids, the thermal conductivity closer to theoretical value. Solid-state sintering densification obtains porous Cu matrix with W-W contiguity and the phenomenon is severer with the increase of W content, the thermal conduction structure is in good agreement with Randall's model. Ni additive is beneficial to densify the Cu matrix. The obtained coefficient of thermal expansion (CTE) through two kinds of densification mechanism are both lower than the theoretical value. The results show that the thermal conductivity and CTE increase with the Cu content, while the relative density trends on the contrary. The surface morphology presents easy to balling due to the instinct property of W and Cu. The roughness and hardness also increase with the increase of W content.

• 出版日期2016-11-5
• 单位北京工业大学