Wilhelmy balance characterization beyond contact angles: Differentiating leaching from nanosurface reorganization and optimizing surface modification

作者：Wang Chenyu; Nair Sithara; Wynne Kenneth J^*

来源：Polymer, 2017, 116: 565-571.

DOI：10.1016/j.polymer.2017.01.047

• Wilhelmy plate method
• Dynamic contact angles
• Polymer surface science

Over and above measurements of contact angles, this article provides examples from our work that emphasize unexpected wetting behavior using the Wilhelmy Plate (WP) method. These findings either would not have been noticed by conventional sessile drop methods or might have been dismissed due to deviations associated with measurements or sample-to-sample variations in surface composition. The examples chosen for this article include: (1) Wilhelmy plate force distance curves providing a sensitive measure for the detection of leaching or diffusion of species from polydimethylsiloxane elastomeric coatings, (2) A Dynamic Contact Angle (DCA) investigation of a polyurethane to establish whether changes in CAs vs immersion time were due to leaching of substances that changed the surface tension of water or to nanosurface reorganization of polymer chains, (3) Changing network formation conditions that give low or high receding contact angles (theta(R)) and "sticky or slippery" wetting of water drops on a widely used Sylgard 184 silicone coating as well as the impact of theta(R) on ice adhesion and (4) Polymer surface modification for introducing special functionality via a modifier is shown to depend on a balance of miscibility and immiscibility that resulted in an unexpected "more is less" dependence on concentration for a fluorous modifier and a condensation cured silicone.

• 出版日期2017-5-5