Size control and catalytic activity of bio-supported palladium nanoparticles

作者：Sobjerg Lina Sveidal; Lindhardt Anders T; Skrydstrup Troels^*; Finster Kai; Meyer Rikke Louise

来源：Colloids and Surfaces B: Biointerfaces , 2011, 85(2): 373-378.

DOI：10.1016/j.colsurfb.2011.03.014

• Palladium
• Recovery
• Bio-palladium
• Cupriavidus
• Staphylococcus
• Nanoparticles

The development of nanoparticles has greatly improved the catalytic properties of metals due to the higher surface to volume ratio of smaller particles. The production of nanoparticles is most commonly based on abiotic processes, but in the search for alternative protocols, bacterial cells have been identified as excellent scaffolds of nanoparticle nucleation, and bacteria have been successfully employed to recover and regenerate platinum group metals from industrial waste.
We report on the formation of bio-supported palladium (Pd) nanoparticles on the surface of two bacterial species with distinctly different surfaces: the Gram positive Staphylococcus sciuri and the Gram negative Cupriavidus necator. We investigated how the type of bacterium and the amount of biomass affected the size and catalytic properties of the nanoparticles formed. By increasing the biomass:Pd ratio, we could produce bio-supported Pd nanoparticles smaller than 10 nm in diameter, whereas lower biomass:Pd ratios resulted in particles ranging from few to hundreds of nm.
The bio-supported Pd nanoparticle catalytic properties were investigated towards the Suzuki-Miyaura cross coupling reaction and hydrogenation reactions. Surprisingly, the smallest nanoparticles obtained at the highest biomass:Pd ratio showed no reactivity towards the test reactions. The lack of reactivity appears to be caused by thiol groups, which poison the catalyst by binding strongly to Pd. Different treatments intended to liberate particles from the biomass, such as burning or rinsing in acetone, did not re-establish their catalytic activity. Sulphur-free biomaterials should therefore be explored as more suitable scaffolds for Pd(0) nanoparticle formation.