Morphological effects on the thermoelectric properties of Ti0.3Zr0.35Hf0.35Ni1+delta Sn alloys following phase separation

作者：Appel Oshrat^*; Zilber Tsvika; Kalabukhov Sergey; Beeri Ofer; Gelbstein Yaniv

来源：Journal of Materials Chemistry C, 2015, 3(44): 11653-11659.

DOI：10.1039/c5tc03214h

Thermoelectrics are known as one of the emerging renewable power generation technologies. Half-Heusler based semiconducting intermetallic compounds show high potential as thermoelectric materials due to the abundance of their elements in nature, their high mechanical and chemical stability, and their favorable electronic properties. Their main limitation lies in their high lattice thermal conductivity, k(l). In the current research, the potential of kl reduction due to generation of composites based on phase separation of off-stoichiometric Ti0.3Zr0.35Hf0.35Ni1+delta Sn alloys into half-and full-Heusler composites was investigated. Due to the strong metallic nature of the full-Heusler phase, its electronic effect on the thermoelectric transport properties under various morphological and compositional conditions was analyzed by the general effective media (GEM) approach. It was shown that although a major kl reduction of up to similar to 37% was associated with phonon scattering by the embedded full Heusler phase, the electronic properties for the parallel-like alignment of this phase, following arc melting and spark plasma sintering, deteriorated with increase of the relative amount of this phase. Therefore a maximal ZT enhancement of similar to 41%, compared to the uni-phase HH stoichiometric composition, was obtained for the minimal (delta = 0.01) deviation of the stoichiometry examined, corresponding to the minimal relative amount of the scattered FH phase inside the HH matrix.

• 出版日期2015