Alloy optimisation of bainitic steel for large plastic mould

作者：Zhang, Z.^*; Wu, X-C.; Li, N.; Min, Y-A.

来源：Materials Science and Technology, 2015, 31(14): 1706-1714.

DOI：10.1179/1743284714Y.0000000744

• Mould steel
• Alloy design
• Bainite
• Retained austenite
• Proeutectoid ferrite

Based on the phase transformation theories, especially the T-0 concept of bainite transformation, alloy optimisation of bainitic steel with carbides has been carried out aiming at the produce of plastic mould with large cross-section. The effect of manganese and silicon on proeutectoid ferrite and bainite transformation is explored by dilatometric analysis, XRD and different microscopy techniques. The results show that after the alloy optimisation, the transformation of proeutectoid ferrite is suppressed and when the cooling rate is lower than 0.18 degrees C s(-1), the new lower bainite transformation appears by decreasing carbon capacity of austenite and promoting carbide precipitation. Industrial production proves that the optimised alloy SDP1 can meet the demand for the plastic mould with the thickness of 1050 mm.

• 出版日期2015-11
• 单位上海大学