Double cantilever beam (DCB) specimens fabricated from a graphite/epoxy (G0814/913) woven prepreg containing a straight through notch were tested by means of constant amplitude fatigue. The specimen was composed of 15 layers with fibers alternating between the weft and warp in the 0 degrees/90 degrees and the +45 degrees/-45 degrees directions. Eight fatigue tests were carried out to determine the delamination growth rate da/dN vs the nearly mode I cyclic energy release rate Delta G(I). Comparison of the delamination growth rate was made to the crack propagation rate of an aluminum alloy. It was found that a crack in the aluminum will grow faster but will be less sensitive to uncertainties or changes in load level.