Anti-Corrosion and Tribo-Mechanical Properties of Co-deposited Zn-SnO2 Composite Coating

作者：Fayomi Ojo Sunday Isaac^*; Popoola Abimbola Patricia Idowu

来源：Acta Metallurgica Sinica (English Letters), 2015, 28(4): 521-530.

DOI：10.1007/s40195-015-0228-6

• Metal matrix composite
• Co-deposition
• Mechanical property
• Corrosion resistance

Zn-SnO2 composite coatings were prepared by direct potential using electrolytic co-deposition technique from sulfate solution. The effect of Zn2+ and SnO2 concentrations in deposited bath on the mechanical properties and morphological characteristics of the composite coatings were examined. The characterizations of the sample were analyzed using scanning electron microscopy couple with energy dispersive spectroscopy (SEM/EDS), X-ray diffraction (XRD) and atomic force microscopy (AFM). The electrochemical degradation behavior of the samples in 3.65 wt.% NaCl solution was studied using potentiodynamic polarization technique and characterized by high-resolution optical microscope. From all the fabricated composite coatings, obvious diffraction peaks were observed with Zn-7Sn-S-0.3V film with Zn2Sn7, Sn, Zn2Sn5 and Zn phases, confirming the presence and formation of Zn-SnO2 coating. The XRD pattern shows that the presences of SnO2 particle remarkably play a major role in the precipitation and orientation of the alloy matrix. From the SEM/EDS and AFM results, the deposits show that composite particle and proper bath composition have strong influence on the microstructure. An enhanced corrosion resistance was attained as a result of the induced particles.

• 出版日期2015-4