The structure and magnetic properties of orthorhombic DyMnO3 nanoparticles with different particle sizes are investigated in this paper. With decreasing particle size, all the lattice parameters a, b, and c gradually decrease, whereas the orthorhombic distortion increases. Magnetic measurements reveal that the antiferromagnetic interaction of Mn ions is weakened due to the decrease in Mn-O-Mn bond angle. Above a critical field H*, DyMnO3 undergoes a field-induced metamagnetic transition at 4 K, which is related to the spin reversal of Dy moments. The critical field H* increases monotonically with size reduction, indicating an enhancement of the antiferromagnetic interaction of Dy ions due to the decreased distance between rare earth ions. The magnetization at 4 K and 5 T, i.e., M(4 K, 5 T) shows a non-monotonic variation with particle size d, i.e., M(4 K, 5 T) initially increases with size reduction but decreases again for d < 68 nm. A modified core-shell model, in which the ferromagnetic ordering (Dy magnetic structure) and antiferromagnetic ordering (Mn magnetic structure) coexist in the core, is proposed to explain this behavior.
- 出版日期2014-9-14
- 单位中国科学技术大学