Analysis of Self-Adhesive Resin Cement Microshear Bond Strength on Leucite-Reinforced Glass-Ceramic with/without Pure Silane Primer or Universal Adhesive Surface Treatment

作者：Lee Yoon; Kim Jae Hoon; Woo Jung Soo; Yi Young Ah; Hwang Ji Yun; Seo Deog Gyu^*

来源：Biomed Research International, 2015, 2015: 361893.

DOI：10.1155/2015/361893

Objective. To evaluate the microshear bond strength (mu SBS) of self-adhesive resin (SA) cement on leucite-reinforced glass-ceramic using silane or universal adhesive. Materials and Methods. Ceramic blocks were etched with 9.5% hydrofluoric acid and divided into three groups (n = 16): (1) negative control (NC) without treatment; (2) Single Bond Universal (SBU); (3) RelyX Ceramic Primer as positive control (PC). RelyX Unicem resin cement was light-cured, and mu SBS was evaluated with/without thermocycling. The mu SBS was analyzed using one-way analysis of variance. The fractured surfaces were examined using stereomicroscopy and scanning electron microscopy (SEM). Results. Without thermocycling, mu SBS was highest for PC (30.50 MPa +/- 3.40), followed by SBU (27.33 MPa +/- 2.81) and NC (20.18 MPa +/- 2.01) (P < 0.05). Thermocycling significantly reduced mu SBS in SBU (22.49 MPa +/- 4.11) (P < 0.05), but not in NC (20.68 MPa +/- 4.60) and PC (28.77 MPa +/- 3.52) (P > 0.05). PC and NC predominantly fractured by cohesive failure within the ceramic and mixed failure, respectively. Conclusion. SBU treatment improves.. SBS between SA cement and glass ceramics, but to a lower value than PC, and the improvement is eradicated by thermocycling. NC exhibited the lowest.. SBS, which remained unchanged after thermocycling.

• 出版日期2015