摘要
In this paper semisolid slurry of Al-6.3Zn-1.9Mg-1.8Cu-0.15Zr alloy with different levels of Sc was prepared, and the effect of Sc content on the morphology of microstructure and mechanical properties of the rheo-diecasting samples was investigated. The results indicate that the excellent semisolid slurry of the wrought Al alloy could be obtained with the addition of 0.22%Sc. Sc additions not only influenced the morphology of the primary alpha-Al particles in the slurry, but also promoted the formation of fine alpha-Al globules in the solidification process of the remaining liquid, which contributed to the considerable improvement in tensile strength and elongation. The tensile strength and elongation of the rheo-diecasting samples with 0.45%Sc after T6 heat treatment increased by 82% and 147% respectively compared to the die-casting samples of the base alloy.