Composite Membranes with Sulfonic and Phosphonic Functionalized Inorganics for Reduced Relative Humidity PEM Fuel Cells

作者：Wang Chunmei^*; Chalkova Elena; Lee Jeong K; Fedkin Mark V; Komarneni Sridhar; Lvov Serguei N

来源：Journal of the Electrochemical Society, 2011, 158(6): B690-B697.

DOI：10.1149/1.3576136

Nafion/inorganic (inorganic S-ZrO2, SiO2-SO3H, SBA-15-SO3H, MCM-41-SO3H, and P-Si gels) composite membranes were synthesized with the goal of increasing the proton exchange membrane (PEM) fuel cell performance at elevated temperatures up to 120 degrees C and reduced relative humidity (RH) down to 25%. Inorganic materials were incorporated within the Nafion by three different techniques. The conductivity of composite membranes with sulfonated inorganic materials was not higher than the conductivity of the recast Nafion in the whole range of inorganic loading. Conductivity of the Nafion/P-Si gel membranes was affected by the surface of inorganic powders and was higher for membranes prepared by in situ formation techniques. At 120 degrees C and 70% RH, the conductivity of some composite membranes reached 100 mS cm(-1). Effect of the inorganic phase on the membrane performance in a fuel cell was much stronger than on its conductivity probably due to substantial improvement in membrane water retention properties. At 120 degrees C and 50% RH, the cell resistance of the P-Si composite membrane was found to be 40% lower than that of Nafion. By applying the modified rule of mixtures, the composite proton conductivity was calculated and compared with experimental data.

• 出版日期2011