Adsorption and surface reaction of bis-diethylaminosilane as a Si precursor on an OH-terminated Si (001) surface

作者：Baek Seung Bin; Kim Dae Hee; Kim Yeong Cheol^*

来源：Applied Surface Science, 2012, 258(17): 6341-6344.

DOI：10.1016/j.apsusc.2012.03.033

• Bond dissociation energy
• Adsorption
• Surface reaction
• Bis-diethylaminosilane
• Atomic layer deposition
• Density functional theory

The adsorption and the surface reaction of bis-diethylaminosilane (SiH2[N(C2H5)(2)](2), BDEAS) as a Si precursor on an OH-terminated Si (0 0 1) surface were investigated to understand the initial reaction mechanism of the atomic layer deposition (ALD) process using density functional theory. The bond dissociation energies between two atoms in BDEAS increased in the order of Si-H, Si-N, and the rest of the bonds. Therefore, the relatively weak Si-H and Si-N bonds were considered for bond breaking during the surface reaction. Optimum locations of BDEAS for the Si-H and Si-N bond breaking were determined on the surface, and adsorption energies of 0.43 and 0.60 eV, respectively, were obtained. The Si-H bond dissociation energy of the adsorbed BDEAS on the surface did not decrease, so that a high reaction energy barrier of 1.60 eV was required. On the other hand, the Si-N bond dissociation energy did decrease, so that a relatively low reaction energy barrier of 0.52 eV was required. When the surface reaction energy barrier was higher than the adsorption energy, BDEAS would be desorbed from the surface instead of being reacted. Therefore, the Si-N bond breaking would be dominantly involved during the surface reaction, and the result is in good agreement with the experimental data in the literature.

• 出版日期2012-6-15