Mechanical and Morphological Properties for Sandwich Composites of Wood/PVC and Glass Fiber/PVC Layers

作者：Mongkollapkit Narudol; Kositchaiyong Apisit; Rosarpitak Vichai; Sombatsompop Narongrit^*

来源：Journal of Applied Polymer Science, 2010, 116(6): 3427-3436.

DOI：10.1002/app.31882

• thermoplastics
• reinforcement
• mechanical properties
• processing

This work manufactured sandwich composites from glass fiber/poly(vinyl chloride) (GF/PVC) and wood/PVC layers, and their mechanical and morphological properties of the composites in three GF orientation angles were assessed. The effects of K value (or viscosity index) of PVC and Dioctyl phthalate (DOP) loading were of our interests. The GF/PVC was used as core layer whereas wood/PVC was the cover layers. The experimental results indicated that PVC with low K value was recommended for the GF/PVC core layer for fabrication of GF/WPVC sandwich composites. The improvement of PVC diffusion at the interface between the GF and the PVC core layer was obtained when using PVC with K value of 58. This was because it could prevent de-lamination between composite layers which would lead to higher mechanical properties of the sandwich composites, except for the tensile modulus. The sandwich composites with 0 degrees GF orientation possessed relatively much higher mechanical properties as compared with those with 45 degrees and 90 degrees GF orientations, especially for the impact strength. Low mechanical properties of the sandwich composites with 45 and 90 GF orientation angles could be overcome by incorporation of DOP plasticizer into the GF/PVC core layer with the recommended DOP loadings of 5-10 parts per hundred by weight of PVC components.

• 出版日期2010-6-15