The effect of Electro Discharge Machining (EDM) on the corrosion resistance of dental alloys

作者：Ntasi Argyro; Mueller Wolf Dieter; Eliades George; Zinelis Spiros^*

来源：Dental Materials, 2010, 26(12): E237-E245.

DOI：10.1016/j.dental.2010.08.001

• Corrosion
• Dental alloys
• X-ray EDS
• Electro Discharge Machining (EDM)

Objective. The aim of the present study was to evaluate the effect of Electro Discharge Machining (EDM) on the corrosion resistance of two types of dental alloys used for fabrication of implant retained superstructures.
Methods. Two groups of specimens were prepared from a Co-Cr (Okta-C) and a grade II cpTi (Biotan) alloys respectively. Half of the specimens were subjected to EDM with Cu electrodes and the rest were conventionally finished (CF). The corrosion resistance of the alloys was evaluated by anodic polarization in Ringer's solution. Morphological and elemental alterations before and after corrosion testing were studied by SEM/EDX. Six regions were analyzed on each surface before and after corrosion testing and the results were statistically analyzed by paired t-test (a = 0.05).
Results. EDM demonstrated inferior corrosion resistance compared to CF surfaces, the latter being passive in a wider range of potential demonstrating higher polarization resistance and lower I(corr) values. Morphological alterations were found before and after corrosion testing for both materials tested after SEM analysis. EDX showed a significant decrease in Mo, Cr, Co, Cu (Co-Cr) and Ti, Cu (cpTi) after electrochemical testing plus an increase in C.
Significance. According to the results of this study the EDM procedure decreases the corrosion resistance of both the alloys tested, increasing thus the risk of possible adverse biological reactions.

• 出版日期2010-12