A 5.5% efficient co-electrodeposited ZnO/CdS/Cu2ZnSnS4/Mo thin film solar cell

作者：Ge, Jie; Jiang, Jinchun^*; Yang, Pingxiong; Peng, Cheng; Huang, Zhipeng; Zuo, Shaohua; Yang, Lihong; Chu, Junhao

来源：Solar Energy Materials and Solar Cells, 2014, 125: 20-26.

DOI：10.1016/j.solmat.2014.02.020

• Cu2ZnSnS4
• Kesterite
• Thin film solar cells
• Co-electrodeposition

Thin film solar cells with a structure of ZnO/CdS/Cu2ZnSnS4 (CZTS)/Mo were fabricated successfully by sulfurization of co-electrodeposited Cu-Zn-Sn-S precursors at 590 degrees C for 15 min. The best solar cell performance was achieved with an efficiency of 5.5% (V-oc=673.8 mV, J(sc)=18.7 mA cm(-2), FF=44%). The vibrational properties and phase identification of the absorber were studied by the polarised Raman and IR spectra. The CZTS absorber layer shows a hi-layered structure comprising of a well-crystallized photovoltaic layer with metallic ratios of Cu/Zn=1.95 and Zn/Sn=1.56 and a particulate-like bottom layer with a heavily Sn poor content. These particulates in the bottom CZTS layer feature with a high density of stacking faults along with ZnS phases and contribute to the low minority lifetime, the high recombination losses, and the increased series resistances in the device. In the well-crystallized CZTS absorber layer the trace of a twin defect on {1 1 2} plane is discovered. Dark electrical analysis indicates there is a relatively small energy barrier height of 44 meV across the cell.

• 出版日期2014-6
• 单位华东师范大学; 上海太阳能电池研究与发展中心