An experimental methodology compliant with industrial constraints was deployed to uncover the origin of soft breakdown events in large planar silicon-based NMOS capacitors. Complementary advanced failure analysis techniques were advantageously employed to localize, isolate and observe structural defects at nanoscale. After an accurate localization of the failing area by optical beam-induced resistance change (OBIRCH), focused ion beam (FIB) technique enabled preparing thin specimens adequate for transmission electron microscopy (TEM). Characterization of the gate oxide microstructure was performed by high-resolution TEM imaging and energy-filtered spectroscopy. A dedicated experimental protocol relying on iterative FIB thinning and TEM observation enabled improving the quality of electron imaging of defects at atom scale. In that way, the gate oxide integrity was evaluated and an electrical stress-induced silicon epitaxy was detected concomitantly to soft breakdown events appearing during constant voltage stress. The growth of silicon hillocks enables consuming a part of the breakdown energy and may prevent the soft breakdown event to evolve towards a hard breakdown that is catastrophic for device functionality.
- 出版日期2014-4