摘要
The influence of laser welding on fatigue crack growth (FCG) behavior of a newly developed nickel-base superalloy, Haynes 282 was studied. Laser welding resulted in cracking in the heat affected zone (HAZ) of the alloy during welding and FCG test results show that this produces deleterious effect on the fatigue crack growth behavior of Haynes 282. However, two post weld heat treatments, including a new thermal treatment schedule developed in this work, are used to significantly improve the resistance of the Haynes 282 fatigue crack growth after laser welding. The effects of laser welding and thermal treatments are discussed in terms of HAZ cracking and heterogeneity of slip, respectively.
- 出版日期2015-1