A poly(vinylidene fluoride)/ethyl cellulose and amino-functionalized nano-SiO2 composite coated separator for 5 V high-voltage lithium-ion batteries with enhanced performance

作者：Zuo, Xiaoxi^*; Wu, Jinhua; Ma, Xiangdong; Deng, Xiao; Cai, Jiaxin; Chen, Qiuyu; Liu, Jiansheng; Nan, Junmin^*

来源：Journal of Power Sources, 2018, 407: 44-52.

DOI：10.1016/j.jpowsour.2018.10.056

• Poly (vinylidene fluoride)/ethyl cellulose
• Amino-functionalized nano-SiO2
• Composite coated separator
• Enhanced performance
• Lithium-ion battery

A poly(vinylidene fluoride)/ethyl cellulose and amino-functionalized nano-SiO2 (PVDF-EC-(A-SiO2)) composite coated on polyethylene (PE) is developed as the functional separator of 5 V high-voltage lithium ion batteries with enhanced performance. Compared with the PE separator, the composite membrane has a uniform interconnected structure, an increased melting temperature from 138 degrees C (PE) to 140.8 degrees C, a decreased contact angle from 49.5 degrees to 23.2 degrees, and higher ionic conductivity from 0.34 mS cm(-1) to 0.79 mS cm(-1). In particular, the electrochemical window is raised to 5.3 V (vs. Li/Li+). LiNi0.5Mn1.5O4/Li batteries with this separator display a high discharge capacity of 131.6 mAh g(-1) and a superior cycling stability with a capacity retention of 95.7% after 200 cycles at 0.5 C. Those results demonstrate that the PVDF-EC-(A-SiO2)/PE composite separator exhibits a good-performance in cycling stability and thermal stability, implying promising potential application in high voltage lithium ion batteries.

• 出版日期2018-12-15