Stress corrosion cracking of a Zr-based bulk metallic glass

作者：Gostin Petre Flaviu^*; Eigel Dimitri; Grell Daniel; Uhlemann Margitta; Kerscher Eberhard; Eckert Juergen; Gebert Annett

来源：Materials Science and Engineering A-Structural Materials Properties Microstructure and Processing, 2015, 639: 681-690.

DOI：10.1016/j.msea.2015.05.049

• Mechanical characterisation
• Bulk amorphous alloys
• Casting
• fracture
• Shear bands

The stress corrosion cracking behaviour of the bulk glassy Zr52.5Cu17.9Al10Ni14.6Ti5 alloy (Vitreloy 105) in 0.01 M Na2SO4+0.01 M NaCl electrolyte was investigated under static three-point bending and anodic potentiostatic control by means of in situ stress and current measurements and subsequent fractography analysis. Pitting takes place preferentially at edges of flat rectangular samples and those pits act as precursors to cracking. Features corresponding to shear banding, mechanical brittle cracking and anodic dissolution assisted cracking were found on the fracture surface. The presence of striations indicates a discontinuous step-wise crack propagation mode. A mechanism is proposed in which crack tip blunting is attributed to shear banding and re-sharpening is attributed to preferential anodic dissolution along shear bands.

• 出版日期2015-7-15