Decalcification resistance of alkali-activated slag

作者：Komljenovic Miroslav M^*; Bascarevic Zvezdana; Marjanovic Natasa; Nikolic Violeta

来源：Journal of Hazardous Materials, 2012, 233: 112-121.

DOI：10.1016/j.jhazmat.2012.06.063

• Alkali-activated slag
• Decalcification
• Accelerated leaching

This paper analyses the effects of decalcification in concentrated 6 M NH4NO3 solution on mechanical and microstructural properties of alkali-activated slag (AAS). Portland-slag cement (CEM II/A-S 42.5 N) was used as a benchmark material. Decalcification process led to a decrease in strength, both in AAS and in CEM II, and this effect was more pronounced in CEM II. The decrease in strength was explicitly related to the decrease in Ca/Si atomic ratio of C-S-H gel. A very low ratio of Ca/Si similar to 0.3 in AAS was the consequence of coexistence of C-S-H(I) gel and silica gel. During decalcification of AAS almost complete leaching of sodium and tetrahedral aluminum from C-S-H(I) gel also took place. AAS showed significantly higher resistance to decalcification in relation to the benchmark CEM II due to the absence of portlandite, high level of polymerization of silicate chains, low level of aluminum for silicon substitution in the structure of C-S-H(1), and the formation of protective layer of polymerized silica gel during decalcification process. In stabilization/solidification processes alkali-activated slag represents a more promising solution than Portland-slag cement due to significantly higher resistance to decalcification.

• 出版日期2012-9-30