Nanoparticulate NaA zeolite composites for MRI: Effect of iron oxide content on image contrast

作者：Gharehaghaji Nahideh; Divband Baharak^*; Zareei Loghman

来源：Journal of Magnetism and Magnetic Materials, 2018, 456: 136-141.

DOI：10.1016/j.jmmm.2018.02.013

• Contrast
• MRI
• Nano iron oxide content
• Nano NaA zeolite

In the current study, Fe3O4/NaA nanocomposites with various amounts of Fe3O4 (3.4, 6.8 & 10.2 wt%) were synthesized and characterized to study the effect of nano iron oxide content on the magnetic resonance (MR) image contrast. The cell viability of the nanocomposites was investigated by MTT assay method. T2 values as well as r2 relaxivities were determined with a 1.5 T MRI scanner. The results of the MTT assay confirmed the nanocomposites cytocompatibility up to 6.8% of the iron oxide content. Although the magnetization saturations and susceptibility values of the nanocomposites were increased as a function of the iron oxide content, their relaxivity was decreased from 921.78 mM(-1) s(-1) for the nanocomposite with the lowest iron oxide content to 380.16 mM(-1) s(-1) for the highest one. Therefore, Fe3O4/NaA nanocomposite with 3.4% iron oxide content led to the best MR image contrast. Nano iron oxide content and dispersion in the nanocomposites structure have important role in the nanocomposite r2 relaxivity and the MR image contrast. Aggregation of the iron oxide nanoparticles is a limiting factor in using of the high iron oxide content nanocomposites.

• 出版日期2018-6-15