Microstructure evolution and mechanical properties of ceramic shell moulds for investment casting of turbine blades by selective laser sintering

作者：Wei, Qian; Zhong, Jiangwei; Xu, Zilin; Xu, Qingyan^*; Liu, Baicheng

来源：Ceramics International, 2018, 44(11): 12088-12097.

DOI：10.1016/j.ceramint.2018.03.227

• Ceramic shell mould
• SLS
• Mullite
• Mechanical properties

Ceramic shell moulds fabricated by traditional shell-making technology have relatively low strength, and often crack during the casting process due to the low strength. In addition, the traditional shell-making process requires long period and high cost. In this work, qualified mullite ceramic shell moulds with enhanced strength were fabricated by selective laser sintering (SLS) combined with high-temperature sintering process. The effects of SLS process parameters on dimensions were investigated, and process optimization was proposed by orthogonal experiments. The effect of sintering temperature on strength at room temperature and 900 degrees C were studied. X-ray diffraction analysis (XRD) and scanning electron microscopy (SEM) analysis suggested that mullitization behavior was influenced by sintering temperature. Furthermore, the content of mullite phase, mullite grain sizes, and mean length-diameter ratio of the mullite grains increased with the sintering temperature. Mechanical testing results showed that the samples sintered at 1610 degrees C had an excellent compressive strength of 99.01 MPa at room temperature and over 172.02 MPa at 900 degrees C. These values far exceed those of ceramic shell moulds fabricated by the traditional shell-making process (40.43 MPa).

• 出版日期2018-8-1
• 单位清华大学