An Al-7.6 at.% Mg alloy was ball milled in liquid N(2) for 8 h and its microstructures were investigated using transmission electron microscopy. Electron diffraction confirmed that the resulting powder is a supersaturated Al-Mg solid solution with an fcc structure. Three typical nanostructures with different grain-size ranges and shapes were observed and the deformation mechanisms in these structures were found to be different. High densities of dislocations were found in large crystallites, implying that dislocation slip is the dominant deformation mechanism. The dislocations rearranged to form small-angle subboundaries upon further deformation, resulting in the formation of medium-sized crystallites with diameters of 10 - 30 nm. In very small crystallites with dimensions less than 10 nm, twinning becomes an important deformation mechanism. The reasons for the different deformation mechanisms were discussed. Some defects, such as twin boundaries, and small- and large-angle grain boundaries were investigated in detail.
- 出版日期2003