Dispersion and soap-free emulsion polymerization of tert-butyl acrylate with the living character and controlled particle size mediated by cobalt porphyrin

作者：Zhao, Huanqin; Wang, Baolong; Li, Qingpan; Wang, Liying^*; Sun, Junmin; Zhang, Yongfeng; Ji, Lichun; Cao, Zhenzhu

来源：RSC Advances, 2017, 7(17): 10124-10131.

DOI：10.1039/c6ra28325j

• TRANSFER RADICAL POLYMERIZATION
• VINYL-ACETATE
• AMBIENT-TEMPERATURE
• MOLECULAR-WEIGHT
• COMPLEXES
• METHACRYLATE
• WATER
• NANOPARTICLES
• STYRENE
• LRP

Living radical polymerization (LRP) of tert-butyl acrylate (tBA) was carried out via dispersion and soap-free emulsion polymerization mediated by cobalt porphyrin [cobalttetramethoxyphenylporphyrin, (TMOP)Co(II)] and initiated by 2,2'- azobis[2-( 2- imidazolin-2-yl) propane] dihydrochloride (VA-044), respectively. The living character was demonstrated by the linear first-order kinetics with different feeding ratios of tBA and (TMOP) Co(II) and a linear increase in the number-average molecular weight was observed with the monomer conversion, as well as the relatively narrow polydispersity. However, only few studies have been reported on (TMOP) Co(II) mediating a living radical dispersion or soap-free emulsion polymerization of tBA. In addition, the obtained poly(tert-butyl acrylate) (PtBA) particles exhibited good uniformity and controlled particle size whether in the dispersion system or in the soap-free emulsion polymerization.

• 出版日期2017
• 单位内蒙古工业大学