Living, Isoselective Polymerization of 4-Methyl-1,3-pentadiene and Styrenic Monomers and Synthesis of Highly Stereoregular Block Copolymers via Sequential Monomer Addition

作者：Capacchione Carmine^*; Saviello Daniela; Ricciardi Rosa; Proto Antonio

来源：Macromolecules, 2011, 44(20): 7940-7947.

DOI：10.1021/ma201442w

The living, isoselective polymerization of 4-methyl-1,3-pentadiene, 4-methylstyrene, and 4-tert-butylstyrene was promoted by using the titanium complex 1 activated by methylaluminoxane (MAO) at room temperature producing highly isotactic polymers. The synthesis of highly isotactic polystyrene-block-poly(4-methyl-1,3-pentadiene), poly(4-methylstyrene)-b/ock-polystyrene, poly(4-methylstyrene)-block-1,4-trans-poly(1,3-butadiene), poly(4-methylstyrene)-block-polystyrene-b/ock-po1y(4-methylstyrene), poly(4-methylstyrene)-block-polystyrene-block-poly(4-methyl-1,3-pentadiene), and poly(4-methylstyrene)-block-polystyrene-block-poly(4-tert-butylstyrene) copolymers was also accomplished for the first time, by sequential monomer addition, in the presence of the system 1 activated by MAO. The thermal features of these polymers dearly show that all copolymer blocks, except the 4-methylstyrene one, are crystalline with melting point values typical of the corresponding homopolymers. The synthesis of a low molecular weight polystyrene sample allowed us to detect the polymer chain ends, giving useful information about the polymerization mechanism.

• 出版日期2011-10-25