Accelerated hydrolytic degradation of Poly(L-lactide)/Poly(D-lactide) stereocomplex up to late stage

作者：Tsuji Hideto^*; Tsuruno Tomonori

来源：Polymer Degradation and Stability, 2010, 95(4): 477-484.

DOI：10.1016/j.polymdegradstab.2010.01.008

• Poly(lactide)
• Poly(lactic acid)
• In vitro autocatalytic hydrolysis
• Stereocomplex
• Enantiomeric polymer blends

Poly(L-lactide) (PLLA)/poly(D-lactide) (PDLA) blend specimens containing only stereocomplex as crystalline species, together with those of pure PLLA and PDLA specimens, were prepared by solution crystallization using acetonitrile as the solvent. Their accelerated hydrolytic degradation was carried out in phosphate-buffered solution at elevated temperatures of 70-97 degrees C Up to the late stage. During hydrolytic degradation, the stereocornplex crystalline residues were first traced by gel permeation chromatography. Similar to the hydrolytic degradation of pure PLLA and PDLA specimens, the hydrolytic degradation of stereocomplexed PLLA/PDLA blend specimens slowed down at the late stage when most of the amorphous chains were removed and crystalline resides were formed and degraded. The estimated activation energy for hydrolytic degradation of stereocornplex crystalline residues (97.3 kJ mol(-1)) is significantly higher than 75.2 kJ mol(-1) reported for alpha-form of PLLA crystalline residues. This indicates that the stereocomplex Crystalline residues showed the higher hydrolysis resistance compared to that of alpha-form of PLLA crystalline residues.

• 出版日期2010-4