Unveiling the Role of CNTs in the Phase Formation of One-Dimensional Ferroelectrics

作者：Mahajan Amit; Reaney Ian M; Costa Pedro M F J; Kingon Angus I; Konya Zoltan; Kukovecz Akos; Vilarinho Paula M^*

来源：Langmuir, 2015, 31(24): 6713-6720.

DOI：10.1021/acs.langmuir.5b00866

Carbon nanotubes (CNTs) have the potential to act as templates or bottom electrodes for three-dimensional (3D) capacitor arrays, which utilize one-dimensional (1D) ferroelectric nanostructures to increase the memory size and density. However, growing a ferroelectric on the surface of CNTs is nontrivial. Here, we demonstrate that multiwalled (MW) CNTs decrease the time and temperature for the formation of lead zirconium titanate Pb(Zr1-xTix)O-3 (PZT) by similar to 100 degrees C commensurate with a decrease in activation energy from 68 +/- 15 to 27 +/- 2 kJ/mol. As a consequence, monophasic PZT was obtained at 575 degrees C for MWCNTs/PZT, but for pure PZT, traces of pyrochlore were still present at 650 degrees C, where the PZT phase formed due to homogeneous nucleation. The piezoelectric nature of MWCNTs/PZT synthesized at 500 degrees C for 1 h was proven. Although further work is required to prove the concept of 3D capacitor arrays, our result suggests that it is feasible to utilize MWCNTs as templates/electrodes for the formation of 1D PZT nanoferroelectrics.

• 出版日期2015-6-23