摘要
Polyaluminum chlorides with a high Al-13 content (PAC-Al-13) and a high Al-30 content (PAC-Al-30) were prepared in a laboratory. The crystalline morphology, SEM images, XRD patterns, aluminum species distribution, and charge neutralization capability of PAC-Al-13 and PAC-Al-30 with a basic ratio (B = [OH-]/[Al3+]) of 2.4 were investigated comparatively. The branching morphology and prismatic crystal images of PAC-Al-13 and PAC-Al-30 were obtained firstly by a simple concentration and crystallization method, and interestingly it was found that these branches appeared to be growing along the diagonal of the tetragonal crystals. The aluminum hydrolytic species distributions of PAC-Al-13 and PAC-Al-30 were quite different: PAC-Al-13 mostly contained the medium polymeric species Alb while the high polymeric species Alc was the main ingredient in PAC-Al-30. PAC-Al-13 and PAC-Al-30 exhibited almost the same charge neutralization capability throughout the investigated dosage range, which demonstrated that the coagulation differences of PAC-Al-13 and PAC-Al-30 investigated in our previous study were probably caused by the stronger bridge-aggregation and sweep-flocculation actions of PAC-Al-30 in the coagulation process. Scanning electron microscopy (SEM) and X-ray diffraction (XRD) were also used to characterize the powder PAC-Al-13 and PAC-Al-30 samples. Moreover, the monomolecular aluminum salt of AlCl3 was investigated in this study as a control.