In vitro hydrolytic degradation of composite quartz fiber-post bonds created by hydrophilic silane couplings

作者：Monticelli F^*; Osorio R; Toledano M; Tay F R; Ferrari M

来源：Operative Dentistry, 2006, 31(6): 728-733.

DOI：10.2341/05-151

The hydrolytic stability of a pre-activated MPS silane (Monobond-S) and a 2-component 4-META/ gamma-MPTS silane (Porcelain Liner M) to H2O2-etched quartz fiber posts was investigated using a modeling approach. Composite build-ups around silanized posts were stored dry for 24 hours, stored in deionized water at 37 degrees C for 24 hours, 1 week, 1 month or they were thermocycled. Sectioned specimens were prepared for microtensile bond testing and SEM examination; 4-META/gamma-MPTS silane produced a rapid decline in bond strength after 1 week and 1 month of water storage and after thermocycling. This was not apparent in pre-activated MPS silane. SEM revealed debonding along the post-composite interfaces, which were coupled with 2-component silane. The use of a hydrophilic resin monomer (4-META) for on-demand hydrolysis of the gamma-MPTS silane expedited interfacial water sorption and hydrolytic degradation, which may be prevented with alternative coupling strategies.

• 出版日期2006-12