Water sorption in hydrogels based on nanocomposites of poly(2-hydroxyethyl acrylate) (PHEA) and silica, prepared by simultaneous polymerization and sol-gel process, were studied gravimetrically over wide ranges of silica content, both below and above the percolation threshold of about 15% wt for the formation of a continuous inorganic network interpenetrated with the organic network. Measurements were performed at room temperature from the vapor phase, both at equilibrium and dynamic, for selected values of water activity alpha(w) between 0 and 0.95, and from the liquid phase. In the nanocomposite hydrogels, the overall water uptake from the vapor phase is practically the same as in pure PHEA below the percolation threshold, whereas it is reduced above the percolation threshold, in particular at high alpha(w) values where swelling becomes significant. Water clustering sets in at around 14 vol % (10 wt %) of water independently of composition, whereas the mean value of water molecules in a cluster decreases at high silica contents. In immersion experiments water uptake decreases as silica content increases to the percolation threshold of about 15 wt % and is then almost independent of composition. A scheme is proposed, which explains these results in terms of the existence of micelles, where a number of hydrophilic hydroxy groups are linked together, and their disentaglement by immersion into water. Diffusion coefficients of water depend on water content and are reduced on addition of silica above the percolation threshold.
- 出版日期2011-5-1