Nonisothermal calorimetric study of the precipitation processes in a Cu-1Co-0.5Ti alloy

作者：Donoso E^*; Zuniga A; Dianez M J; Criado J M

来源：Journal of Thermal Analysis and Calorimetry, 2010, 100(3): 975-980.

DOI：10.1007/s10973-009-0642-y

• Copper alloys
• DSC
• Kinetics
• Precipitation
• Cu-Co-Ti alloys

The precipitation processes in a Cu-1.0 at.%Co-0.5 at.%Ti (Cu-1.5 at.%Co(2)Ti) alloy were studied using differential scanning calorimetry (DSC), transmission electron microscopy (TEM), and microhardeness measurements. The analysis of the calorimetric curves from room temperature to 900 K shows the presence of two exothermic reactions attributed to the formation of CoTi and Co(2)Ti particles in the copper matrix. On the basis of enthalpy calculations, it was found that the decomposition begins with the precipitation of CoTi, followed by the formation of Co(2)Ti particles. The activation energies calculated using the modified Kissinger method were lower than the ones corresponding to diffusion of cobalt and titanium in copper. Kinetic parameters were obtained by a convolution method based on the Johnson-Mehl-Avrami (JMA) formalism. The values obtained for the parameter n were indicative of a particle nucleation process from preexistent nuclei. Microhardness measurements and TEM micrographs confirmed the formation of the mentioned phases.

• 出版日期2010-6