Hierarchically Porous Carbon Encapsulating Sulfur as a Superior Cathode Material for High Performance Lithium-Sulfur Batteries

作者：Xu Guiyin; Ding Bing; Nie Ping; Shen Laifa; Dou Hui; Zhang Xiaogang^*

来源：ACS Applied Materials & Interfaces, 2014, 6(1): 194-199.

DOI：10.1021/am4038728

• lithium-sulfur batteries
• hierarchical porous carbon
• composite
• cycling performance
• high loading

Lithium-sulfur (Li-S) batteries are deemed to be a promising energy storage device for next-generation high energy power system. However, insulation of S and dissolution of lithium polysulfides in the electrolyte lead to low utilization of sulfur and poor cycling performance, which seriously hamper the rapid development of Li-S batteries. Herein, we reported that encapsulating sulfur into hierarchically porous carbon (HPC) derived from the soluble starch with a template of needle-like nanosized Mg(OH)(2). HPC has a relatively high specific surface area of 902.5 m(2) g(-1) and large total pore volume of 2.60 cm(3) g(-1) resulting that a weight percent of sulfur in S/HPC is up to 84 wt %. When evaluated as cathodes for Li-S batteries, the S/HPC composite has a high discharge capacity of 1249 mAh g(-1) in the first cycle and a Coulombic efficiency as high as 94% with stable cycling over prolonged 100 charge/discharge cycles at a high current density of 1675 mA g(-1). The superior electrochemical performance of S/HPC is closely related to its unique structure, exhibiting the graphitic structure with a high developed porosity framework of macropores in combination with mesopores and micropores. Such nanostructure could shorten the transport pathway for both ions and electrons during prolonged cycling.

• 出版日期2014-1-8
• 单位南京大学